• 应经常观察水箱内、外部主件及配件使用情况，箱体如有碰伤、划痕会出现水锈，应采用柔软的布料擦拭后上蜡即可；

Should always observe the water tank, the main parts and accessories used in the box body, such as scratches, nicks will appear rust, should use soft cloth to wipe after waxing;

• 水箱底部支架需定期检修，发现锈蚀需重新进行防锈处理，严重的需及时更换；

The bottom of the water tank bracket need regular maintenance, found corroded necessary anti-rust treatment, serious change;

• 不锈钢水箱一般每年需要清洗、保养两次，以保持水箱内的清洁，保护水箱；水箱清洗保养前关闭进水阀，打开排污孔堵头(或阀门)，使水箱中的余水排尽；用干净拖把或抹布对水箱周边和底部进行清洗，底部积垢严重的，可用软毛巾加清洁剂擦洗；较长时间使用水箱必须清洗污浊，打开进水阀门，放入适量清水冲洗箱壁及底部，使污垢从排污口排净，必要时可反复进行多次，直到满意为止，旋紧排污堵头，打开进水阀门，让水箱重新装满水，清洗工作结束水箱即可直接使用（管道在水箱清洗后相应进行排放清理）。

Stainless steel water tank the general annual need cleaning, maintenance of two times, in order to keep the tank clean, protect the water tank; tank cleaning and maintenance before closing the water inlet valve, open the drain hole plug (or valve), so that the residual water in the water tank is discharged; clean the water tank and the bottom of the surrounding with a clean mop or cloth, at the bottom of the serious fouling use a soft towel, add detergent scrub; use for a long time the tank must be clean dirty, open the inlet valve, add appropriate amount of water washing tank wall and bottom, so that the dirt from the sewage outfall drain, when necessary, can be repeated several times, until satisfied, tighten the drain plug, open the inlet valve, let the water refill with water the cleaning tank, the end can be used directly (pipe in the water tank cleaning after the corresponding discharge cleaning).

• 不锈钢水箱箱体和暴露于大气中的其他物体一样，也会脏，所以，不锈钢水箱尤其不得使用于工厂烟囱下方，*空调排气板附近或废旧钢厂，石矿厂附近；在定期清洗或做其他施工时，不得使用硬物（如钢丝球，金属榔头等）撞击其表面，以防伤及“钝化膜"，加速其腐蚀程度；

Stainless steel water tank cavity and exposure to other objects in the atmosphere, will be dirty, so, stainless steel water tank especially do not use in the factory chimneys below, near the central air-conditioning exhaust plate or waste steel, quarry near; in regular cleaning or other construction, shall not use the hard objects (such as steel wire, metal hammer etc. the impact of the surface), to prevent injuries "passivation", accelerate the corrosion degree;

• 由于不锈钢热敏感性较强，在450-850度温度区域内停留时间过长，因热影响区域耐腐蚀性严重下降，故非专业人员不得进行施工或修补；

Because the stainless steel thermal sensitivity of strong, long residence time in 450-850 temperature region, serious decline because of the heat affected zone corrosion resistance, so the non - professional personnel shall not for the construction or repair;

• 如在使用过程中出现问题要预先通知厂家技术维修人员，维修焊接人员，要求是专门从事氩弧焊接工作的专业人员，维修时要把水放掉方可操作。

Such as in the use of process problems should notice manufacturers technical repair personnel, repair welding personnel, is specialized in argon arc welding for working professionals, Repair to turn the water off before the operation.